Abstract
In the present study, polycrystalline Co50V34Ga16−xFex (1≤x≤2) quaternary Heusler alloys were fabricated by the arc-melting method. It was found that they undergo a paramagnetic martensitic transformation (MT) from the L21-type cubic austenitic structure to the D022 tetragonal martensitic structure. With the increase of the Fe concentration, the MT shifts towards a higher temperature range, which is strongly related to the variation of the valence electron concentration. Moreover, it was also found that the MT exhibited by every alloy is sensitive to the applied hydrostatic pressure due to a relatively high difference in volume between the two phases. By using the quasi-direct method based on caloric measurements, the barocaloric effect (BCE) associated with the hydrostatic pressure-driven MT was estimated in the studied alloys. The results demonstrated that the sample with x=1.5 performs an optimal BCE among these three alloys.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.