Abstract
Martensite structures in Ti-rich Ti-Ni thin films were investigated. It was found that the existence of GP zones with coherency or Ti 2 Ni precipitates with semi-coherency produces the formation of ( 001) compound twins as internal twinning. The structure consists of three domains in different orientations, each of which contains the (001) twins. These domains are related to each other by a (111) twinning orientation relationship, but the boundaries between the domains are divided into three types: (111) type, (001)//(1111) type and nearly (11 3)-type The last type of boundary was defined as a mixture of (001)//(111) and (1 11)//( 001) boundaries. The martensite structures in specimens with GP zones and Ti 2 Ni precipitates are basically the same, but the martensite domain of the former specimen is much larger than that Ofthe latter one. This is because the domains grow and pass through the GP zones by elastic deformation of the GP zones, while they stop in front of the Ti 2 Ni precipitates or nucleate at the matrix-precipitate interfaces.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.