Abstract
ObjectivesTo compare the marginal gap and fracture resistance of implant-supported 3-dimensional (3D) printed definitive composite crowns with those fabricated by using 3 different millable materials. Material and methodsA prefabricated abutment was digitized by using a laboratory scanner (E4 Lab Scanner) and a complete-coverage maxillary first premolar crown was designed (Dental Designer). Forty crowns were fabricated either by 3D printing (Saremco Print Crowntec, SP) or milling (Brilliant Crios, BC; Vita Enamic, VE; Cerasmart 270, CS) (n = 10). Baseline marginal gap values were evaluated by measuring 60 predetermined points on an abutment (15 points for each side) with a stereomicroscope at ×40 magnification. Marginal gap values were reevaluated after adhesive cementation. Load-to-fracture test was performed by using a universal testing machine. Two-way analysis of variance (ANOVA) was used to evaluate the effect of material type and cementation on marginal gap values. While Tukey HSD tests were used to compare the materials’ marginal gap values before and after cementation, the effect of cementation on marginal gap values within each material was analyzed by using paired samples t-tests. Fracture resistance data were analyzed by using 1-way ANOVA (α=0.05). ResultsMaterial type and cementation significantly affected marginal gap values (P < .001). Regardless of cementation, SP had the lowest marginal gap values (P < .001), while the differences among milled crowns were nonsignificant (P ≥ .14). Cementation significantly increased the marginal gap values (P < .001). Material type did not affect fracture resistance values (F = 1.589, P = .209). ConclusionImplant-supported 3D-printed composite crowns showed higher marginal adaptation compared with the milled crowns before and after cementation. In addition, all crowns endured similar forces before fracture.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.