Marginal adaptation and fracture resistance of milled and 3D-printed CAD/CAM hybrid dental crown materials with various occlusal thicknesses.

Abstract

To evaluate the marginal adaptation and fracture resistance of three computer-aided design/computer-assisted manufacturing hybrid dental materials with different occlusal thicknesses. Ninety single-molar crowns were digitally fabricated using a milled hybrid nanoceramic (Cerasmart, CE), polymer-infiltrated ceramic network (PICN, Vita Enamic, VE), and 3D-printed materials (Varseosmile, VS) with occlusal thicknesses of 0.8, 1, and 1.5 mm (10 specimens/group). Anatomical 3D-printed resin dies (Rigid 10K) were used as supporting materials. A CEREC MCX milling unit and a DLP-based 3D printer, Freeform Pro 2, were utilized to produce the crown samples. Before cementation, the marginal adaptation, absolute marginal discrepancy (AMD), and marginal gap (MG) were assessed using micro-CT scanning. After cementation with self-adhesive resin cement, fracture resistance was evaluated using a universal testing machine. The number of fractured crowns and the maximum fracture values (N) were recorded. Data were statistically analyzed using both one- and two-way ANOVA, followed by Tukey's honestly significant difference (HSD) test. For all occlusal thicknesses, the VS crowns demonstrated the lowest AMD and MG distances, significantly different from those of the other two milling groups (P < 0.05), whereas CE and VE did not differ significantly (P > 0.05). All VS crowns were fractured using the lowest loading forces (1480.3±226.1 to 1747.2±108.7 N). No CE and 1 and 1.5 mm VE crowns fractured under a 2000 N maximum load. All hybrid-material crowns demonstrated favorable marginal adaptation within a clinically acceptable range, with 3D printing yielding superior results to milling. All materials could withstand normal occlusal force even with a 0.8 mm occlusal thickness.