Abstract
Hot pressing and spark plasma sintering were applied to manufacture electrical discharge machinable ZTA-TiC ceramics containing 17 vol.% zirconia (1.5Y) and 24 vol.% titanium carbide in an alumina matrix. Sintering was carried out at 1450–1600 °C and 40 MPa pressure with 2 h dwell for HP and 10 min for SPS. The influence of sintering conditions on mechanical properties, microstructure, phase composition and electrical conductivity was investigated. Both sintering technologies lead to fully densified samples with similar strength and toughness. Hardness was generally lower for SPS. SPS samples develop a finer microstructure. HP samples the TiC grains tend to merge at high sintering so that HP materials reach significantly higher conductivities. Productivity and energy consumption per piece can be significantly decreased by shifting to SPS. Both types of material were ED-machinable. Hot pressed ceramics showed better cutting performance and improved surface quality in trimming operations.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.