Abstract
The continuous glass fiber reinforced polylactic acid (PLA) prepreg was manufactured by direct melt impregnation. The mechanical and thermal properties of PLA prepreg were observed. The properties of PLA prepreg were compared with the neat PLA and the injection molded glass fiber/PLA composite. The PLA prepreg having a fiber volume fraction of 27.7 % shows well enhanced tensile strength of 331.1 MPa, flexural strength of 528.6 MPa, and flexural modulus of 24.0 GPa. The enhancement in the heat deflection temperature (HDT) and the crystallinity were also observed. The fracture interface was inspected by FE-SEM. The degree of impregnation as a function of pulling speed was measured. The degree of impregnation at the pulling speed of 5 m/min reached over 90 % in this research.
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.