The SiCp performing sample was made first then Al/SiCp (65%) was manufactured. Appropriate component and proportion of binder and process parameters were selected to control the porosity. Debinding has succeeded by extractive and thermal debinding processes. SiCp preforming samples with good appearance, enough strength, and right porosity were obtained by pre-sintering process at 1100°C. Composites with high density and homogeneous microstructure were manufactured by pressure infiltration under 1050°C and 15MPa. The distribution of aluminium and silicon elements was homogeneous. The primary components of materials are aluminium, β-SiC and α-SiC. The thermal expand coefficient of composites is 8.0×10-6/°C at room temperature, which increases with temperature and reaches to 11.0×10-6/°C at 300°C. The density is 2.92g/cm3, and relative density is more than 97 %. The strength is about 500MPa, approaching to the upper limit of the theoretical value.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.