Abstract
The manufacturing and optimization of centrifugally casted ceramic membrane supports is presented. For the optimization, the effect of three different powder sizes (0.25, 0.31 and 0.61 μm) and a sintering temperature range between 1050 and 1400 °C was investigated. The ceramic tubes were characterized according to tube dimensions, mercury porosimetry, water permeability, SEM and mechanical strength. It was shown that the centrifugal casting technique delivers highly reproducible support properties. A novel strength testing apparatus was developed to determine the mechanical strength of the ceramic tubes. It was found that the strength varied between 3300 MPa and 300 MPa, depending on the porosity of the supports. With increased sintering temperature, water permeability and porosity decreased, while strength and linear shrinkage increased. The pore diameter of the supports produced by the 0.31 and 0.61 μm powders decreased, while that of the 0.25 μm powders remained constant (72 nm) with increasing sintering temperature. The 0.61 μm powder sintered at the lowest sintering temperature resulted in the support with the highest porosity, pore diameter and porosity, but the lowest mechanical strength and linear shrinkage. An overall improvement concerning pure water permeability was seen when the support in this study was compared to our own previous studies and similar studies in literature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.