Abstract
In this paper, 0.6(Na0.5Bi0.5)TiO3–0.4NaNbO3(0.6NBT–0.4NN) was synthesized by solid state reaction method. The homogenous green ceramic sheets with high density were produced by tape casting according to suitable casting parameters. Embryos of multilayered ceramic capacitors (MLCC) had been fabricated by punching, screen printing, stacking, laminating and cutting processes. And then after burning out and sintering at different conditions, the cross-sectional microstructures of components were compared. Differential scanning calorimetric analysis and the thermo-gravimetric analysis of green devices were carried out to analyze the effects of different sintering procedures on MLCCs. The dielectric properties and polarization loops of the MLCCs were investigated with dielectric constant (800–895), dielectric loss (0.004–0.007) and capacitance variation ΔC/C < 11 % in the temperature range of −55 to 205 °C, which satisfied X9R in the Electronic Industries Association standard. The breakdown strength of the capacitor was 260 kV/cm. The resistance of the capacitor was measured to be 1.873 × 1011 Ω. These properties of the 0.6NBT–0.4NN ceramic capacitor indicated the potential dielectric materials for the application of MLCCs at the high temperature.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Materials Science: Materials in Electronics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.