Abstract
The morphology of CdSe/SiO(2) was manipulated from core-shell-structured nanoparticles to nanocables by using a chemical vapor deposition (CVD) process. The growth of nanocables, with cores no more than 20 nm in diameter, is initiated by the formation of core-shell nanoparticles with SiO(2) as matrix and CdSe clusters dispersed inside. After the subsequent vaporization of the SiO(2) matrix, the follow-up CdSe vapor crystallizes with the remaining CdSe clusters as nuclei to form CdSe nanowires as the furnace was cooled to 1200 degrees C. During the controlled cooling of the furnace, the SiO vapor re-deposits to sheathe the nanowires. The thickness of the shell and the diameter of core were successfully controlled. The photoluminescence measurements show that the CdSe/SiO(2) nanocables have strong visible-light emission bands located at 590 and 688 nm, which are attributed to the defects induced by SiO(2) sheaths nanowires and the quantum confinement effect of the CdSe, respectively. The UV/Vis absorption spectra of the naked CdSe nanowires further validate the above-mentioned quantum confinement effect. The deterministic growth of these nanocables is very important for the design of the nanodevices based on them.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.