Manifestation of anharmonicities in terms of Fano scattering and phonon lifetime of scissors modes in α-MoO3.

Abstract

α-MoO3 exhibits promising potential in the field of infrared detection and thermoelectricity owing to its exceptional characteristics of ultra-low-loss phonon polaritons (PhPs). It is of utmost importance to comprehend the phonon interaction exhibited by α-MoO3 in order to facilitate the advancement of phonon-centric devices. The intriguing applications of α-MoO3 for phonon-centric technology are found to be strongly dependent on scissors Raman modes. In this study, we have investigated the temperature-dependent asymmetric Raman line-shape characteristics of two scissors modes, Ag(1) and B1g(1), in the orthorhombic phase of bulk α-MoO3 within a temperature range spanning from 138 K to 498 K at 633 nm excitation wavelength. The Fano-Raman line-shape function was employed to analyze the asymmetry in terms of electron-phonon coupling strength, which varies from 0.050 to 0.313 and -0.017 to -0.192 for Ag(1) and B1g(1) modes, respectively, with temperature. This asymmetric behavior of Ag(1) and B1g(1) scissors modes are attributed to interference between the electronic energy continuum and discrete TO and LO phonon states, respectively. Therefore, the line-shape asymmetry in two scissors modes with increasing temperature stemming from the Fano resonance is also consistent with a 488 nm excitation wavelength. Additionally, anharmonicity caused by temperature results in redshift, and linewidth broadening of these two scissors modes through cubic-phonon decay has been observed. Moreover, the ultrashort lifetime of these optical phonons diminishes from ∼1.37 ps to ∼0.53 ps with increasing temperature due to the dominance of cubic-phonon decay over quartic-phonon decay. Our findings strongly emphasize the significance of investigating anharmonic interactions with Fano resonance to acquire an extensive comprehension of the vibrational characteristics of α-MoO3 for novel functionalities.