Magnetostriction of Fe81Ga19 oriented crystals

Abstract

The effect of the orientation on the magnetostriction in Fe81Ga19 alloy has been investigated experimentally and theoretically. The Fe81Ga19 [001] and [110] oriented crystals were prepared and the magnetostriction was measured under different pre-stress. The saturation magnetostriction of the [001] oriented crystal increases from 170 × 10−6 to 330 − 10−6 under the pre-stress from 0 to 50 MPa. The [110] oriented crystal has a saturation magnetostriction from 20 × 10−6 to 140 × 10−6 with the compressive pre-stress from 0 to 40 MPa. The magnetostriction of [001] and [110] oriented crystals has been simulated based on the phenomenological theory. The domain rotation path has been determined and the resultant magnetostriction calculated under different pre-stress. The experimental and simulated results both show that the [001] oriented crystal exhibits better magnetostriction than [110] oriented crystal. The enhancement of the saturation magnetostriction by the compressive pre-stress in the [110] oriented crystal is higher than that in the [001] oriented crystal.