Abstract
The magnetoimpedance (MI) of Fe92−x−yZr7BxCu1Aly (x=2,4,6,8,y=0,0.5,1,1.5) alloys has been measured to investigate the influence of the structural changes in the crystallization process as well as the changes of the soft magnetic properties such as permeability, magnetic anisotropy, etc. after thermal treatment. The MI measurements were carried out along the ribbon axis with longitudinal magnetic field. The nanocrystalline alloy system was prepared by the rapid quenching technique in an Ar atmosphere. Ultrasoft magnetic behavior has been observed in all samples annealed at 550 °C. The x-ray diffraction and transmission electron microscopy results show the α-Fe phase appeared in the annealed alloy system at 550 °C. The maximum magnetoimpedance ratio value in Fe84Zr7B3Cu1 alloy annealed at 550 °C was reached as much as 1100%. The field annealing does not contribute to improve the magnetoimpedance effect in these nanocrystalline alloy system.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.