Abstract
Multiferroic Ba1.6Sr1.4Co2Fe24O41 with a Z-type hexagonal structure was obtained through the proteic sol-gel process with a single-phase, combined with thermal treatment at 1200 °C for 2 h. XRD analysis revealed the formation of a single phase, with preferential orientation in the case of a sample in pellet form. Magnetometry measurements revealed a low coercive field characteristic of Z-type hexaferrite, plus an electrical resistivity of approximately 2 × 109 Ω.cm that was considerably higher than expected.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.