Abstract
Contrasting magnetic properties were obtained from bulk Mn-doped ZnO synthesized under different processing conditions. While a ferrimagnetic phase transition was observable in a Zn0.95Mn0.05O sample processed at 1170 K, no such transition was found for a sample with the same composition processed at 1370 K. The detailed magnetic, structural, and spectroscopic studies of these two samples have revealed that the ferrimagnetic transition in the former sample is attributable to the secondary phase, (Mn,Zn)Mn2O4, in the system. For the latter sample processed at higher temperature, no secondary phase was detected and the major feature of the system remained paramagnetic down to 4 K. The implication of the present results for Mn-doped ZnO thin films is discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.