Abstract
We measured the dc magnetization, electrical resistivity, and ac magnetic susceptibility of a series of polycrystalline CePt 3 Si samples whose compositions vary slightly from the stoichiometric composition. The sample that showed the most distinct antiferromagnetic transition at 2.2 K was found to be Ce 1.01 Pt 3 Si annealed. This sample showed a clear bulk antiferromagnetic order at 2.2 K even in both electrical resistivity and dc magnetization measurements, although the characteristic change in dc magnetization at 2.2 K was found to be small and to be easily masked in other magnetic anomalies if they exist. Moreover, it had the largest residual resistivity ratio. We concluded that Ce 1.01 Pt 3 Si annealed has the intrinsic bulk properties of ideal CePt 3 Si. In addition, we revealed that some anomalies arise as a result of the variation in composition. One is a ferromagnetic anomaly at 3.0 K in the Pt-rich samples, and the other is an antiferromagnetic anomaly at 4.0 K in the Pt-poor samples. The two m...
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call