Abstract
Nickel ferrite thin films were synthesized at room temperature using one-step electrodeposition solution processing. Reaction kinetics was also proposed. An effect of air baking on the structural, surface morphological and magnetic properties was investigated. As-deposited nickel ferrite thin films were cubic in crystal structure. Calculated grain size after annealing was increased from 30 to 48 nm in addition to formation of rough surface morphology. Due to decrease in defect levels after air baking the annealed nickel ferrite thin film showed saturation magnetization of 268 emu/cc, higher than non-annealed (230 emu/cc), when used in magnetic studies.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.