Abstract
Nanocrystalline La0.50Ba0.50MnO3 manganite was synthesized by an optimized sol-gel method. The initial sample was subjected to step-by-step heat treatment under air atmosphere. The ion stoichiometry, the morphology of crystallites of ceramics, and the magnetic properties were studied. It is established that the average crystallite size increases with increasing annealing temperature. All of the samples studied are characterized by a perovskite-like cubic structure, with the unit cell parameter a increasing continuously with the average crystallite size. The most significant lattice compression occurs in the sample with an average crystallite size of ~ 30 nm. The increase in the average crystallite size causes a nonmonotonic increase in the Curie temperature and in the spontaneous magnetic moment. The anomalous behavior of the magnetic properties of the La0.50Ba0.50MnO3 manganites obtained is explained by the competition between two size effects, namely, the frustration of the indirect exchange interactions Mn3+ – O – Mn4+ on the nanocrystallite surface and the crystal lattice compression due to the crystallite surface tension.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.