Abstract
Bismuth layer-structured compounds in the Bi-Ti-Fe-O system known as Aurivillius phases are single phase multiferroics. It was stated that substitution of some rare earth elements for bismuth ions in such structure can modified its magnetic properties. Powders of Bi7Fe3Ti3O21 and Bi6.3Sm0.7Fe3Ti3O21 were prepared by co-precipitation – calcination method and then were sintered to dense polycrystalline materials. Low field DC susceptibility was measured in the zero field cooled (ZFC) and field cooled (FC) modes at 10÷350 K. For selected temperatures magnetisation curves and hysteresis loops were also measured. The FC and ZFC curves of both samples diverge at temperatures below 250 K indicating a spin glass-like behaviour. The compound with samarium exhibits magnetic hysteresis already at room temperature with the coercive field increasing to 870 Oe at 10 K. The low temperature hysteresis loops of the samarium containing compound are shift with respect to zero field which can be attributed to a magneto-electrical coupling of the samarium sublattice "exchange biased" by the iron one, which orders anti-ferromagnetically at a higher temperature than the samarium sublattice.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.