ABSTRACTWe report on the growth and magnetic properties of single crystal Mn-doped GaN, InGaN, and AlGaN films. The III-Nitride films were grown by MOCVD, while the Mn doping was performed by solid-state diffusion of a surface Mn layer deposited by pulsed laser ablation. Mn-doped InxGa1-xN films were grown with x < 0.15, where the easy axis of magnetization rotates from in-plane to out-of-plane by changing the InxGa1-xN thickness/strain-state of the film from compressively strained to relaxed. Mn-doped AlxGa1-xN films were grown with x < 0.40 showing ferromagnetic behavior above room temperature. SQUID measurements ruled out superparamagnetism within these films. By optimizing the growth and annealing conditions of Mn-doped III-Nitrides, we have achieved Curie temperatures in the range of 228 to 500K. These ferromagnetic Mn-doped III-Nitride films exhibit hysteresis with a coercivity of 100–500 Oe. TEM analysis showed no secondary phases within these films.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.