Abstract

Nanocomposite of Co-SiO/sub 2/, a soft magnetic material, with Co weight fraction x = 0.3 and 0.7 was prepared via mechanical milling. The magnetic properties of these samples, both zero-field-cooled (ZFC) and field-cooled (FC), have been measured as a function of x, milling time, and temperature. The structural assessment of the composite indicates a presence of only ferromagnetic hcp/fcc-Co phase in the composite. However, reported magnetic properties of these composites appear to be dependent on the presence of antiferromagnetic phases of cobalt oxide as well. The FC magnetic measurements show a presence of an exchange bias field and an enhanced coercivity which are higher than the ZFC measurements. All magnetic measurements indicate that the overall magnetic properties of the composite are dictated by the presence of a trace amount of cobalt oxides which remain undetected in XRD.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.