Abstract
Fe(x)Pt(y)Au(100-x-y) nanoparticles of size 3.5 nm were prepared by polyol reduction of platinum acetylacetonate and gold acetate and the thermal decomposition of iron pentacarbonyl. The as-synthesized nanoparticles with disordered fcc structure were then heat treated to transform to the L1(0) structure with high magnetocrystalline anisotropy. By tuning the stoichiometry of the Fe(x)Pt(y)Au(100-x-y) nanoparticles, the phase transition temperature was reduced by more than 200 degrees C. After the annealing 500 degrees C, for instance, the highest coercivity of 18 kOe was obtained from the Fe51Pt36Au13 nanoparticles which is substantially higher compared to 2 kOe for Fe51Pt49 nanoparticles annealed at the same temperature. In addition to the high coercivity, the saturation magnetization value obtained from Fe51Pt36Au13 nanoparticles was 47 emu/g which is similar to that for the Fe51Pt49 nanoparticles, indicating that there is no trade-off between the coercivity and the saturation magnetization upon Au doping.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.