Abstract
The magnetic properties and the microstructures of HDDR magnet materials fabricated from the alloys with chemical composition of Nd 14 Fe bal Co 15 B 6.5 Nb x Zr y (x = 0-0.25; y = 0-0.25) have been investigated. The variation of the magnetic properties of the magnets with HD temperature and DR temperature was studied. The results show that HD temperature and DR temperature affect the magnetic properties of HDDR magnet powders obviously. The analysis of XRD spectra shows that the process of HDDR technique is hydrogenation disproportionation desorption recombination. The addition of a small amount of Nb element is useful to improve the magnetic properties of HDDR magnetic powders. And the composite addition of a little Nb and Zr can further enhance the magnetic properties. The reasons for the enhancement of the magnetic properties by the composite addition of small amounts of Nb and Zr are analyzed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.