Abstract
The magnetic properties and structural phase transformations of Heusler alloys Ni/sub 2+x/Mn/sub 1-x/Ga and Ni/sub 2-x/Mn/sub 1+x/2/Ga/sub 1+x/2/ were investigated. It was found that the martensitic transformation temperature increases and the Curie temperature decreases with decreasing Mn concentration in the Ni/sub 2+x/Mn/sub 1-x/Ga system, but the magnetic properties decrease faster than those do in the Ni/sub 2-x/Mn/sub 1+x/2/Ga/sub 1+x/2/ system. This suggests that the influence of the conduction electron concentration and the distance between Mn atoms on the Curie temperature is stronger than the magnetic dilution effect. The martensitic transformation temperature shows a peak value at x=0.06 in the Ni/sub 2-x/Mn/sub 1+x/2/Ga/sub 1+x/2/ system. A large stress-free magnetic-field-induced strain (MFIS) of 1.8% has been obtained at room temperature in a single crystal sample with the composition of the first system.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.