Abstract
Silica–hematite (α-Fe2O3) nanocomposites were synthesized by addition of aqueous solution containing ferrous ions (Fe2+), cetyltrimethylammonium bromide (CTAB) as a surfactant and tert-butanol (t-butanol) as a cosurfactant into colloidal silica solution. At alkaline atmosphere, silica surface with negative charges electrostatically attracts positively-charged iron hydroxide nuclei or particles which are stabilized by cationic CTAB molecules, and then silica–iron compound composites could be formed. Finally, the silica–hematite composite particles were obtained after calcination at 800 °C for 4 h. Through these processes, two types of composites having “core–shell type” or “decorated type” could be achieved. Morphology, BET surface area, crystallinity and magnetic properties of samples were analyzed by using TEM, BET, XRD and VSM, respectively. The “decorated type” composites had larger BET surface area and better magnetization. Also, to estimate the application in water treatment, adsorption properties of composites were studied through methylene blue (MB) adsorption which was characterized by UV–vis spectroscopy, involving collection of composites with neodymium magnet.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.