Abstract
The magnetic field stability of the PrFeB magnets is one of the key points which affect its application in such devices as cryogenic permanent magnet undulators. In this study, the magnetic properties and microstructure of PrFeB magnets, which were developed by the grain boundary diffusion, were examined. The demagnetizing field distribution of the cryogenic permanent magnet undulator made using the PrFeB magnets was simulated by Radia, and the change mechanism of the irreversible demagnetization following treatments at high temperatures was experimentally studied. The results show that the intrinsic coercivity of the PrFeB magnets can be increased by diffusion of Tb. Meanwhile, the remanence of the magnets displays almost no loss, and the increasing range is closely related to the orientation thickness of the PrFeB magnet. Therefore, the PrFeB magnets developed using grain boundary diffusion are found to have extremely high comprehensive magnetic properties. The irreversible demagnetization of the PrFeB magnets developed by grain boundary diffusion for the CPMU is determined to be significantly improved following high-temperature treatments.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.