Abstract
Magnetic, electronic transport and magneto-transport behaviours of (Co1−xMnx)2P (0.55 ⩽ x ⩽ 0.675) compounds have been systematically investigated. A typical metallic-conductivity behaviour is observed in the ferromagnetic compound (Co0.45Mn0.55)2P. The increase in the Mn concentration gives rise to dramatic changes in magnetic, electronic transport and magneto-transport behaviours. With increasing temperature, a first-order phase transition from antiferromagnetism to ferromagnetism takes place at about 145 K, 185 K and 240 K for x = 0.60, 0.625 and 0.65, respectively. (Co0.4Mn0.6)2P and (Co0.375Mn0.625)2P compounds experience a metal-insulator transition (Anderson transition) with decreasing temperature. An external magnetic field of 5 T strongly influences the Anderson transition, lowering the transition temperature from 80 to 55 K for (Co0.4Mn0.6)2P and from 115 to 70 K for (Co0.375Mn0.625)2P. In contrast with this metal-insulator transition, an insulating behaviour appears in the temperature range from 10 to 300 K for (Co0.35Mn0.65)2P and (Co0.325Mn0.675)2P compounds. Below the antiferromagnetic–ferromagnetic transition temperature TAF–F, a metamagnetic transition can be induced by an external magnetic field. The metamagnetic transition is accompanied by a maximum magnetoresistance ratio of −7%, −6.3% or −3.7% at 5 T in the (Co0.4Mn0.6)2P, (Co0.375Mn0.625)2P or (Co0.35Mn0.65)2P compound at 10 K. The mechanisms of magnetoresistive behaviours are discussed in terms of the formation of a super-zone gap in the antiferromagnetic state.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have