Abstract
Influence of substrate miscut on magnetization dynamics in SrRuO3 (SRO) thin films was studied. Two films were grown on SrTiO3 substrates with high (∼ 1°) and low (∼ 0.1°) miscut angles, respectively. As expected, high miscut angle leads to suppression of multi-variant growth. By means of SQUID magnetometry, comparable relaxation effects were observed in both the multi-variant and the nearly single-variant sample. Differences in the magnetization reversal process were revealed by magnetic force microscopy. It showed that the multi-variant growth leads to higher density of defects acting as pinning or nucleation sites for magnetic domains, which consequently results in deterioration of magnetic properties. It was demonstrated that the use of high miscut substrate is important for fabrication of high quality SRO thin films with low density of crystallographic defects and excellent magnetic properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.