Abstract
Specific heat, magnetic susceptibility, and neutron scattering have been used to investigate the nature of the spin system in the antiferromagnet Nd3Co4Sn13. At room temperature Nd3Co4Sn13 has a cubic, Pm-3n structure similar to Yb3Rh4Sn13. Antiferromagnetic interactions between, Nd3+ ions dominate the magnetic character of this sample and at 2.4 K the Nd spins enter a long range order state with a magnetic propagation vector q = (0 0 0) with an ordered moment of 1.78(2) µB at 1.5 K. The magnetic Bragg intensity grows very slowly below 1 K, reaching ~2.4 µB at 350 mK. The average magnetic Nd3+ configuration corresponds to the 3D irreducible representation Γ7. This magnetic structure can be viewed as three sublattices of antiferromagnetic spin chains coupled with each other in the 120°-configuration. A well-defined magnetic excitation was measured around the 1 1 1 zone centre and the resulting dispersion curve is appropriate for an antiferromagnet with a gap of 0.20(1) meV.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.