Abstract
Synthesis, X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), Raman spectroscopy and magnetic measurements at low temperature of Ni metallic clusters covered by NiO , Ce2O3and CeO2, obtained from CeNi5powder oxidized in air at different temperatures up to 800°C, are reported. The average crystallite size of Ni core and the thickness of NiO oxide formed at the surface increase with temperature due to recrystallization processes, from 34 nm at 300°C to 77 nm at 800°C and from 9 nm to 19 nm, respectively. Ni metallic component was detected both in XPS valence bands and core levels spectra only after sputtering. The hysteresis loop presents a small shift towards negative magnetic fields which confirms the presence of ferromagnetic Ni /antiferromagnetic NiO interfaces.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.