Magnetic anisotropy and transport properties of 70 nm SrRuO3 films grown on different substrates

Abstract

Magnetic and transport properties of 70 nm SrRuO3 films grown on (001) SrTiO3, (001) LaAlO3 and (001) MgO have been investigated. A perpendicular magnetic anisotropy is observed in compressive strained films grown on SrTiO3. A weaker perpendicular magnetic anisotropy and a weak in-plane magnetic anisotropy are found in strain-free films grown on MgO and LAO, respectively, possibly due to different growth mechanisms. In addition, metallic behavior is observed in all the as-grown films and the resistivity of the film grown on MgO is lowest (230 μΩ cm at 300 K), which is close to that of bulk single crystal SrRuO3 (about 195 μΩ cm). The relation between structure and properties indicates that the magnetic anisotropy, as well as the magnitude of resistivity of SrRuO3 films, can be effectively tailored by taking advantage of different strains and growth mechanisms induced by growth on different substrates.