Abstract
Cobalt–nickel ferrite ( Co 0.5 Ni 0.5 Fe 2 O 4) were prepared using a high energy milling and sintering. The starting raw materials of NiO , Co3 O4 and Fe2O3 were subjected to 12 hr milling using a Spex8000D mixer/mill. The resulting material was molded into samples of toroidal/disc shape and subsequently sintered at various temperatures from 600 to 1000° C, at 100° C interval. The effect of sintering temperature on microstructure, saturation magnetization ( M s), and coercivity ( H c) was reported. The frequency dependence of the magnetic and dielectric properties such as permittivity, loss tangent, permeability and loss factor were investigated in the frequency range of 10 MHz–1.8 GHz. The results show that the real part of the permittivity at individual temperatures was constant within the measured frequency, while the loss tangent values decreased gradually with increasing frequency. The real permeability on the other hand remained fairly constant over certain frequency (around 1.0 GHz), and thereafter increases towards saturation thereby showing a good potential in the microwave frequencies region.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.