Abstract
AbstractTo meet the needs for higher energy efficiency and a wide operating temperature range of electric vehicles, the low‐loss MnZn ferrites in a wide temperature range have been developed by optimizing the Fe content and the oxygen partial pressure (PO2) during the sintering process in this work. For the optimal sample, power loss at 300 kHz/100mT is 204 kW/m3 at 25°C and remains below 290 kW/m3 in the wide temperature range from ‐10 to 120°C. The loss separation method was employed to clarify the effects of the Fe content and PO2 on power loss. The equivalent circuit model has been employed to fit the complex impedance and it is found that the increase of PO2 enhances both the grain resistance Rg and the grain boundary resistance Rgb. The enhancement of Rgb is mainly responsible for the reduction of eddy current loss and consequently power loss. Dielectric permittivity is as large as about 15000 in this series of samples due to the electric polarization at the rich grain boundaries. Dielectric loss is very low between ‐50 and 150°C and has little contribution to the energy loss.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.