Magnetic and anomalous Hall effect investigations of co-sputtered Co2MnGa Heusler alloy thin films

Abstract

The cobalt-based full Heusler alloy Co2MnGa (CMG) is well known for exhibiting an exotic phenomenon such as magnetic Weyl semimetallic nature with a high Curie temperature of ∼700 K and a giant anomalous Hall effect. Here, we report a detailed study of structural, electrical, and magnetic properties of Co2MnGa thin films (thickness in the 40–10 nm range) grown on Si(100) by the direct-current magnetron co-sputtering technique using Co and MnGa targets. Structural analysis of the samples revealed the polycrystalline nature of these films with B2 type structural ordering. The damping parameter decreases with the increase in film thickness and reaches the minimum value of 6.1 × 10−3 for a 40 nm thin CMG film. These CMG films are magnetically isotropic and soft ferromagnetic in nature. A remarkably high value of anomalous Hall conductivity (AHC) of 1920 S/cm (2 K) is found for the 40 nm thin film, which is comparable to earlier reported values on highly ordered CMG films. Nearly 73% of this AHC value originates from the intrinsic contribution. The AHC and longitudinal conductivity both increase with the film thickness. Different scaling mechanisms are used to compute the intrinsic and extrinsic contributions playing a role in AHC. The analysis of advanced scaling [by Tian et al., Phys. Rev. Lett. 103, 1–4 (2009)] performed on these CMG films suggests the consistency in the enhanced intrinsic AHC value irrespective of the thickness and a decrease in skew scattering contribution with thickness. These results will enhance the understanding about the magnetic and transport properties of Co2MnGa thin films of different thicknesses and suggest it to be a promising material for topospintronic applications.