Abstract
A series of the magnesium apatite coatings according to (Ca10-xMgx)(PO4)6(OH)2, where x = 0 to 2, was synthesized through a sol-gel dip-coating method. The roughness of the magnesium coatings increased as more magnesium incorporated into the coatings. The mechanical properties of the coatings were analyzed with Nanoindentor. The incorporation of magnesium decreased the hardness and the Young’s modulus of the coating. The X-ray Photoelectron Spectroscopy (XPS) analysis revealed that only part of magnesium was incorporated into the apatite structure while the rest existed in the form of MgO in the coating.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.