Abstract
This paper investigates the structural homogeneity of samples of articles made of ZhS6U alloy obtained by wire-feed electron beam additive technology. It is found that the formed material is represented by directionally growing dendrites and does not contain any defects. The temperature gradient value and its dependence on the height of the additively formed product are estimated using the change in the primary dendrite arm spacing. On this basis, it is concluded that the temperature gradient values achieved during the additional formation process correspond to the modern methods of directional solidification. The features of the electron-beam additive process that affect the heat removal conditions and cause changes in the temperature gradient are shown. It is found that changes in these conditions do not significantly affect the size and morphology of the intermetallic γ'-phase. It is demonstrated that the mechanical properties of the additively formed product material are superior to those of the original material in the as-cast state.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.