Macro and micro damage analysis and parameter inversion of HTPB adhesive Interface based on DIC and FEMU

Abstract

ABSTRACT In order to realize the quantitative analysis of the structural integrity and damage evolution of hydroxyl-terminated polybutadiene (HTPB) composite solid propellant under external load, the loading failure experiments were carried out on the macro rectangular specimen and the micro specimen, and the numerical analysis of the strain evolution process in the region of interest (ROI) of the specimen was carried out using digital image correlation (DIC). At the same time, with the help of finite element model updating (FEMU) method, the mechanical and cohesion parameters of the specimen were inversed using the combination of adaptive particle swarm optimization (APSO), back propagation (BP) and Hooke-Jeeves algorithm, and the simulation of the whole process of propellant damage and fracture was realized from the microscopic point of view. The results show that inhibiting the debonding of propellant/liner interface is the key to maintain the structural integrity. It starts with the damage and fracture of the propellant side. A scanning electron microscope (SEM) in-situ dynamic tensile test shows that the initial damage occurs at the strain of 27.368%, and the through-type crack propagates along the interface when the strain reaches 43.276%. In addition, the use of combinatorial optimization algorithm can realize the global optimal inversion of 16 parameters divided into three types in 100 complete calculations, reduce the optimal objective function value to 0.0251, and assist the finite element calculation to realize the quantitative analysis and accurate simulation of the experimental process.