Machining Characteristics and Fracture Morphologies in a Copper-Beryllium (Cu-2Be) Alloy

Abstract

The technology of materials removal is improved greatly by the introduction of advanced cutting tools like cubic boron nitride, ceramics, polycrystalline diamond and the more recent whisker-reinforced materials. In this paper, the influence of cutting temperature on machinability, mechanical properties, microstructure, and fracture morphology of Cu-2Be alloy using a polycrystalline diamond cutter is investigated. The information on machining, microstructure, and fracture morphology of Cu-2Be alloy are very useful to understand their fabrication characteristics and the basic mechanisms of its deformation and fracture. The machinability (in terms of surface finish) of Cu-2Be alloy is evaluated as a function of cutting temperature, resulting from wet and dry cutting. Machining is carried out on a Hardinge Cobra 42 CNC machine (Hardinge Inc., Elmira, NY), and the machining parameters used—cutting speed, depth of cut, and feed rate—are kept constant during both wet and dry cutting. The machined surface finish on Cu-2Be alloy is measured using a surface finish analyzer (Surftest 401, series 178) technique. The machined specimens are examined for their strength and hardness properties using a standard Universal Testing Machine and Rockwell hardness tester, respectively. Wet cutting (using coolants) produced a smooth surface finish when compared with dry cutting of the Cu-2Be alloy. The machined specimens are examined for their microstructural features using a Nikon optical microscope. The specimens are etched using a suitable etchant solution for revealing such microstructure constituents as grain size, phase proportions, and the possible overheated areas (especially in dry cutting). The fractured surfaces from the tensile and impact toughness tests are investigated for their fracture morphologies (dry and wet cutting) using a microprocessor-controlled scanning electron microscope (Jeol Model JSM 5910 LV). A detailed analysis is also made to understand and interpret the basic fracture mechanisms responsible for crack initiation and crack propagation. The Cu-2Be alloy showed relatively higher mechanical properties in wet cutting in comparison to dry cutting operations. Fracture studies demonstrated intergranular and ductile fractures as dominant modes of fracture mechanisms in Cu-2Be alloy.