M- S-H formation in MgO-SiO2slurries via wet milling for magnesia based castables

Abstract

It is believed that the formation of hydration phase, MgO-SiO2-H2O (M-S-H), contributes to good workability and reliable comprehensive properties for magnesia based castables. In order to stimulate the formation of M-S-H in magnesia based castables and understand the minimum introduction of microslica amount, wet milling process was used to promote the dissolution of MgO and SiO2 in this work. The slurry containing different content of microsilica with wet milling technology and the castables with/without wet milling slurry were prepared. The effects of microsilica content on the formation of hydration phases were analyzed by XRD, FT-IR and TG/DSC and the properties of magnesia based castables were evaluated by explosion resistance, CMOR, HMOR and so on. The results showed that the formation of M-S-H was accelerated because of the dissolution of Mg2+ and HSiO3− in wet milling process. Higher amount of M-S-H led to a tight bonding in the early stage, and a denser structure after firing at high temperature due to the limited formation of brucite and in-situ formation of evenly distributed forsterite phase. In addition, much higher HMOR were obtained when less microsilica was added, attributing to the suppressed formation of low-melting-point liquid. Therefore, 2–3 wt% microsilica addition was recommended in this process.