Abstract
The surface of an ordered mesoporous silica (OMS) was functionalized using 1H,1H,2H,2H-perfluorooctyltrimethoxysilane at 20â and 60â. It was shown that only elevated temperature allows lyophobic properties on the walls of OMS, eventually preventing pore flooding with nonaqueous electrolytes. The functionalized OMSs (OMS-F) were characterized with various techniques: wettability test, N2 sorption measurement, high-resolution transmission electron microscopy (HR-TEM). Cathodes of 10mg/cm2 loading were prepared with a commercial Pt/C catalyst and polyvinylidene fluoride (PVDF, 2.5 wt.%) binder using a typical doctor blade method on a commercial gas diffusion layer (GDL) in the presence or in the absence of OMS-F additives. Subsequent discharge-charge curves were taken in a 1M LiTFSI-TEGDME electrolyte at 60â in pure oxygen atmosphere. It was found that the discharge capacity was significantly affected by OMS-F: 5 wt.% of additive extended discharge capacity by a factor 1.5. On the other hand, a similar OMS material but synthesized at 20â did not show lyophobic properties and deteriorated cathode capacity. Keywords: Li-air battery, oxygen transport, lyophobic ordered mesoporous silica, perfluorosilane
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.