Abstract
We report on successful preparation of Er3+ doped transparent alumina (0.1–0.17 at.%) exhibiting visible light photoluminescence using wet shaping method and hot isostatic pressing. The effects of dopant amount, type of doping powder and powder pre-treatment on final microstructure, real in-line transmittance and photoluminescence characteristics were studied.The real in-line transmittance ranged between 28 and 56%, depending on processing parameters. The transparency decreased with increased amount of dopant. The decrease is dependent on the type of doping powder and its pre-treatment.The photoluminescence spectra measured in both visible and NIR region showed typical emission bands due to the presence of Er3+ ions. The decay profiles of the 4S3/2→4I15/2 transition were fitted with a 2-exponential function, with faster component in the range of 360–700ns and slower component around 1.6-2.4μs. The intensity of emissions and lifetime of the 4S3/2 level decrease significantly with increasing concentration of Er3+ ions.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.