Abstract
When activated by Dy3+, Na0.25K0.25Bi0.50TiO3 (NKBT), piezoelectric powders show strong luminescence in the blue and yellow spectral range. Emissions of this material can be effectively utilized for both luminescence intensity ratio and lifetime-based readouts of temperature. Photoluminescence measurements over a temperature range of 293–483 K show that the luminescence intensity ratio temperature readout has maximal relative sensitivity of 1.93% K−1 at 380 K, while the relative sensitivity of the lifetime temperature readout reaches 1.1% K−1 at 480 K. For this study, materials were synthesized by a solid-state reaction using TiO2, Bi2O3, Na2CO3, K2CO3 and Dy2O3 as precursors. X-ray diffraction measurements showed that the NKBT sample crystallized in the A-site substituted distorted perovskite rhombohedral structure (R3c symmetry). The photoluminescence spectra showed characteristic emission bands of Dy3+ ions centered at 457 nm (4I15/2 → 6H15/2), 478 nm (4F9/2 → 6H15/2), 574 nm (4F9/2 → 6H13/2) and 663 nm (4F9/2 → 6H11/2). The ratio of emissions from 4F9/2 and 4I15/2 excited states to the 6H15/2 ground state was used as a luminescence intensity ratio indicator of temperature, while the decay of emission from 4F9/2 → 6H13/2 transition was used as a lifetime indicator of temperature. CIE coordinates x = 0.326 and y = 0.361 calculated from room temperature emission spectra show the perspective of this material for use in white light emission devices.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.