Abstract
The compositional dependence of luminescence properties and scintillation response were investigated in Ce3+-doped Y2Gd1Al5-xGaxO12 (x = 2, 3, 4) single crystals. The Gd3+ → Ce3+ energy transfer was evidenced by photoluminescence excitation spectra of Ce3+ emission. With increasing Ga content in the garnet host, the Ce3+ luminescence from the lowest 5d level (5d1) is shifted toward higher energy due to the decrease in the crystal field splitting of the 5d levels. Light yield (LY) and its dependence on the amplifier shaping time were measured under excitation with γ-rays. High LY value of ∼38 000 ph/MeV was obtained for a Y2Gd1Al3Ga2O12:Ce sample. Scintillation decay was measured with an extended dynamical and temporal scale under the nanosecond pulse soft X-ray excitation. The decrease of both LY value and relative contribution of slower decay component in the scintillation response was observed with increasing Ga content in the garnet host.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.