Abstract
Comparison of the luminescent properties of Ca3Sc2Si3O12:Ce and Ca2YMgScSi3O12:Ce single crystalline films (SCF) phosphors, grown by the liquid phase epitaxy method, was performed in this work. We have observed formation of the Ce3+ multicenters in Ca3Sc2Si3O12:Ce and Ca2YMgScSi3O12:Ce in the emission and excitation spectra as well as in the decay kinetics of the Ce3+ luminescence in SCFs of these garnets. Such Ce3+ multicenters possess different crystal field strength due to the inhomogeneous local surroundings of the dodecahedral positions of garnet host at the substitution of the octahedral positions by hetero-valence Mg2+ and Sc3+ ions and the tetrahedral positions by Si4+ ions. We confirm the presence of an effective energy transfer between different Ce3+ multicenters in Ce3+ doped Ca3Sc2Si3O12 and Ca2YMgScSi3O12 garnets. The positive trends in variations of the spectroscopic properties of the Ca2YMgScSi3O12:Ce garnet with respect to Ca3Sc2Si3O12:Ce garnet were observed also due to substitution of the dodecahedral sites of the garnet host by Y3+ ions and the octahedral sites by Mg2+ ions, which can be suitable for the development of new converters of white LEDs. Namely, due to the Y3+-Mg2+ doping, the luminescence spectrum of Ce3+ ions in Ca2YMgScSi3O12:Ce SCFs significantly extends in the red range in comparison with the Ca3Sc2Si3O12:Ce SCF counterpart.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.