Abstract
In the last years, increasing interest has been paid to polyurethane (PU) foams with open porosity to be used as scaffold in numerous tissue engineering applications. In fact, they possess good cyto- and biocompatibility, and they can be synthesized with tunable chemico-physical and mechanical properties by varying the base reagents used for their synthesis (polyol, isocyanate, and expanding agent) and the stoichiometric ratio between them. The aim of this work was to design and develop novel PU foams with high open porosity and tunable physical and mechanical properties by varying the polyol composition and the stoichiometric ratio between the base reagents. PU foams were synthesized by a one step gas foaming method (stoichiometric and not stoichiometric foams), by reacting a polyol mixture ad hoc set up with MDI prepolymer, using Fe-AA as catalyst, and water as expanding agent. Different polyol mixtures were prepared by varying the ratio between the main polyol components, e.g. a polyether-polyol (component A), a polyether-polyol containing styrene (component B), and an amine-based tetrafunctional polyether-polyol (component C). The PU foams were characterized by SEM, micro-CT, ATR-FTIR analysis, and evaluation of density, water uptake, and mechanical properties by uniaxial compressive tests in dry and wet conditions. Polyol composition do not affect PU foam open porosity, while the pore size and water uptake increase with the increase of components B and C. All the foams show higher compressive properties in dry than in wet state, due to the plasticizing effect of water. PU foams synthesized with an excess of diisocyanate are significantly stiffer than the stoichiometric ones. In addition the compressive properties of the PU foams are mostly affected by the amine-based tetrafunctional component, that causes a higher level of cross-linking, stiffness and strenght. Preliminary tests show no cytotoxic effects for all the tested PU foams.
Highlights
Previous works & results by setting up and controlling the foaming process we are able to obtain suitable porous structures, with a high percentage of open porosity the foaming process can be adapted to produce scaffolds with tailored properties for regeneration of tissues with different requirements, like derma, cartilage and bone
Aim of our research to design and develop PU foams as scaffolds for tissue engineering applications with open porosity and tunable physical and mechanical properties by using a previously set up foaming process effects of polyol composition and ratio between base reagents
Influence of polyol composition – mechanical properties uniaxal compressive test in dry & wet condition n=3; Ø=6 mm; h=4 mm deformation ramp 2.5%/min up to 50% & 5%/min up to 0 T=37°C
Summary
PU foams as scaffolds: basic requirements mechanical strength open porosity homogeneous morphology biocompatibility (ability to be biointegrated or bioabsorbed with no toxic effects). Previous works & results by setting up and controlling the foaming process we are able to obtain suitable porous structures, with a high percentage of open porosity the foaming process can be adapted to produce scaffolds with tailored properties for regeneration of tissues with different requirements, like derma, cartilage and bone. Previous works & results in vitro tests with different cell lines & primary cells (fibroblasts, human condrocytes, primary human osteblasts, SAOS 2 and MG63). Foams highly cytocompatible in vitro tests with mesenchymal stem cells (MSCs) from human bone marrow and human placenta ability to support stem cells differentiation into osteoblasts. Foams highly cytocompatible in vitro tests with mesenchymal stem cells (MSCs) from human bone marrow and human placenta ability to support stem cells differentiation into osteoblasts in vivo implantation in subcutaneous tissue of rats up to 42 weeks foams highly biocompatible. Exploiting the versatility of polyurethane to obtain PU foams with tailored properties by varying the foaming parameters, in particular the polyol mixture formulation & the ratio among the PU foam reagents, foams with different properties can be synthesized selection of the appropriate components & their ratio for the polyol mixture formulation
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.