Abstract
Nanocrystalline NbB2 powders were successfully prepared by borothermal reduction in molten salt at 800°C–1000°C. Due to the more homogeneous mixing and more rapid diffusion of species in the liquid state than in the solid state, the synthesis temperature of pure NbB2 phase was greatly decreased by the presence of molten NaCl/KCl salt. The NbB2 powders synthesized at 1000°C had the largest specific surface area of 27.09 m2/g and the lowest equivalent average particle size of 32 nm, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.