Abstract
The memory performance of hafnium oxide (HfO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">x</sub> )-based resistive memory containing a thin reactive Ti buffer layer can be greatly improved. Due to the excellent ability of Ti to absorb oxygen atoms from the HfO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">x</sub> film after post-metal annealing, a large amount of oxygen vacancies are left in the HfO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">x</sub> layer of the TiN/Ti/HfO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">x</sub> /TiN stacked layer. These oxygen vacancies are crucial to make a memory device with a stable bipolar resistive switching behavior. Aside from the benefits of low operation power and large on/off ratio (>100), this memory also exhibits reliable switching endurance (>10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">6</sup> cycles), robust resistance states (200°C), high device yield (~100%), and fast switching speed (<10 ns).
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.