Low transparency current density and high temperature operation from ten-layer p-doped 1.3μm InAs∕InGaAs∕GaAs quantum dot lasers

Abstract

High temperature photoluminescence up to 100°C was demonstrated from the p-doped ten-layer InAs∕InGaAs quantum dot (QD) laser structure. 1.3μm InAs QD lasers were fabricated using pulsed anodic oxidation from this structure. High output power of 882mW and low transparency current density of 5.9A∕cm2∕QD layer were obtained. Ground state (GS) lasing could be maintained from a QD laser with short cavity length of 611μm, corresponding to the maximum modal gain of 23.1cm−1 from this laser system. GS continuous wave operation up to 100°C was also demonstrated from an InAs QD laser (50×2500μm2).