Abstract
Tetragonal BaTiO3 was prepared by reaction of a layered K2Ti2O5 and mixed barium salts (BaCl2 + Ba(NO3)2) at above 700°C. The morphology of the particle was cubic shape and the particle size of the products prepared at 700–1000°C was ∼10 µm, and that of the products prepared at higher temperatures (1100–1200°C) was smaller than that of the products prepared at 700–1000°C. From the chemical analysis no potassium atom was detected and the Ba/Ti ratio in the tetragonal BaTiO3 was 1.00. In the cubic particle of the tetragonal BaTiO3 surface 90° domain boundaries were observed. Lattice parameters and Curie temperature of the tetragonal BaTiO3 were a = 3.995(1) and c = 4.036(1) A and 130°C, respectively.
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.