Abstract
We have synthesized La1-xSrxMnO3 (with x=0.3, 0.33 & 0.4) perovskite nanoparticles using mild sol-gel technique at low temperature and thereby studied the effect of nanosize on magnetoresistance. These samples were characterized using TGA/DSC, XRD, TEM, FTIR and temperature dependent magnetoresistance (MR) measurements. Powder X-ray diffraction (XRD) result confirms the formation of pure crystalline phase with rhombohedral symmetry in R-3C space group. Crystallite size increases with increase in Sr concentration. TEM analysis further supports the nanosized particles in the samples which lie in the range of 20-30 nm. Fourier transform infrared (FTIR) spectroscopy shows a broad peak at 615 cm -1 for all the samples gives an evidence for the formation of metal oxygen bond organized in to MnO6 octahedral. The steep change in magnetoresistance (MR) at low field at low temperature is observed which is attributed to the alignment of the spins, while in the high field MR is due to the grain boundaries effect at low temperature. In the series studied, 33% Sr doped sample shows higher MR both at low temperature (-17.15) and room temperature (-3.07) than their counter parts.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.